Rodent & Termite-Resistant LSOH Sheathing Compound

YHS62012HFSY

This material uses polyolefin elastomer as base resin, compounded with high-efficiency flame retardants, smoke suppressants, antioxidants, anti-rodent & anti-termite agents and processing aids, then mixed, plasticized and pelletized. It delivers excellent physical & mechanical properties, processing performance, good flame retardancy and low-smoke halogen-free environmental features, designed for optical cable outer sheathing applications.

✦ Rodent & termite resistant ✦ LSOH optical sheath ✦ polyolefin elastomer ✦ anti rodent anti termite ✦ optical cable sheathing compound

Technical Data

Technical Specifications

Typical physical property data, subject to batch test reports.

Test project	Units	YHS62012HFSY
Density	g/cm3	1.46
Original tensile strength	MPa	11.8
Original elongation at break	%	185
Air thermal aging	℃×h	+15
Change rate of tensile strength	%	-12
Elongation at break change rate	%	-10
Low temperature	℃	-40 pass
20℃ volume resistivity	Ω·cm	4.0×10¹⁴
20℃ dielectric strength	MV/m	28
Oxygen Index	%	35
High temperature pressure (80℃×4H)	%	10
Thermal shock (150℃×1H)	-	No crack
Smoke density — Flame method	-	70
Smoke density — Flameless method	-	180
Amount of halogen acid gas	mg/g	0
pH value	-	6.4
Conductivity	μS/mm	1.2
Toxicity index	-	1.5

Recommended

Extrusion Process

When the storage environment is wet or the production surface is required to be high, the particles can be dried in a hot air hopper at 70℃ for 1-2 hours.

It is recommended to use a low compression ratio screw extrusion with a compression ratio of 1.2-2.0:1.Before extrusion, the screw should be cleaned to ensure the cleanliness of the product. It is recommended to use 80 mesh or 100 mesh filter screen to avoid impurities in the extrusion process, and to ensure the melt pressure to obtain a good appearance and material density.As the difference between the actual temperature of the melt and the indicated value of the temperature control table varies with the type of extruder, the user is requested to select the appropriate temperature according to the specific situation of the extruder used.The following temperatures can be used as reference for start-up and commissioning:

Position	Cylinder I	Cylinder II	Cylinder III	Cylinder IV	Cylinder V	Head and mold
Temperature (℃)	120±5	140±5	150±5	155±5	155±5	160±5

Processing Guide

Recommended Processing Parameters

(25 ± 0.2) kg / bag, inner aluminum plastic composite bag, outer kraft paper bag (or customer specified packaging)
Stored in dry and ventilated place
Prevent sun, rain and water
Storage period is 6 months