Technical Data
Technical Specifications
Typical physical property data, subject to batch test reports.
| Properties | Value | Unit | Method |
|---|---|---|---|
| Physical Properties | |||
| Hardness(1S) | 69 | Shore D | ISO 868 |
| Melting Flow Index | 11 | g/10min | ISO 1133 |
| Density | 1.26 | g/cm3 | ISO 1183 |
| Mechanical Properties | |||
| Flexural Modulus | 550 | MPa | ISO 178 |
| Tensile Strength at break | 43 | MPa | ISO 527 |
| Tensile Elongation at break | >300 | % | ISO 527 |
| Notched Charpy Impact Strength (23℃) | 22 | KJ/m² | ISO 179 |
| Notched Charpy Impact Strength (-30℃) | 14 | KJ/m² | ISO 179 |
| Thermal Properties | |||
| Melting Point | 218 | ℃ | ISO 11357 |
| Vicat Softening Temperature,10N | 205 | ℃ | ISO 306 |
| UL Flammability rank ,1.60 mm | HB | class | UL 94 |
| Electrical Properties | |||
| Volume Resistivity | 8.0×10¹³ | Ohm·cm | IEC 60093 |
| Surface Resistivity | 7.0×10¹⁵ | Ohm | IEC 60093 |
| Dielectric Strength | 21 | KV/mm | IEC 60243-1 |
| Comparative tracing index | 600 | - | IEC 60112 |
| Other Properties | |||
| Water Absorption (Immersion 24h) | 0.3 | % | ISO 62 |
| Mold Shrinkage | 1.7 | % | ISO 294 |
| Drying condition |
Recommended
Extrusion Process
We recommend drying condition: 110℃ * 3-5hours.
| Molding Type | Melting temperature | Screw temperature | Die temperature | Mold temperature |
|---|---|---|---|---|
| Extrusion | 220-250℃ | 220~245℃ | 240~250℃ | |
| Injection | 225-250℃ | 220~250℃ | 230~250℃ | 35~50℃ |