European-Standard Power Cord Compound

YHS62016J & YHS62016H

Low-smoke halogen-free flame-retardant cable compounds for European standard power cords (YHS62016 series, including YHS62016J insulation material and YHS62016H sheath material) adopt polyolefin elastomer as base resin, incorporated with flame retardants, smoke suppressants, antioxidants and other processing aids, then compounded, plasticized and pelletized. The series delivers outstanding mechanical, electrical, flame retardant and processing properties, featuring halogen-free formulation and low smoke emission. YHS62016J insulation grade complies with HD21.14, featuring excellent anti-blocking performance and insulation property. YHS62016H sheath grade also meets HD21.14, with anti-blocking, soft texture, good elasticity and superior wear resistance. Cables made from this material are soft, resilient and wear-resistant.

✦ Low smoke halogen-free flame retardant ✦ HD21.14 cable compound ✦ European power cord material ✦ Anti-blocking insulation ✦ Flexible sheath material ✦ Wear-resistant polyolefin elastomer

Recommended

Extrusion Process

Note: The above data is a typical value obtained by testing the product and is not a standard for testing restrictions.

Test project	Units	YHS62016J	YHS62016H
Density	g/cm3	1.45	1.40
Hardness	Shore A	90	85
Original tensile strength (after irradiation)	Mpa	11.5	9.5
Original elongation at break (after irradiation)	%	200	280
Air thermal aging (after irradiation)	℃×h	80×168	80×168
Change rate of tensile strength	%	+13	+10
Elongation at break rate	%	-10	-8
Low temperature	℃	-40 pass	-40 pass
20℃ volume resistivity	Ω·cm	5.0×10¹⁴	2.0×10¹⁴
20℃ dielectric strength	MV/m	28	26
Oxygen Index	%	35	33
High temperature pressure (80℃ * 4H)	%	15	22
Thermal shock (130℃ * 1H)	-	No crack	No crack
Smoke density (Flame method)	-	55	60
Smoke density (Flameless method)	-	140	150
Amount of halogen acid gas	mg/g	0	0
pH value	-	6.8	6.6
Conductivity	μs/mm	1.5	1.2
Toxicity index	-	1.0	1.5

Packaging & Storage

Packaging and storage

(25 ± 0.2) kg / bag, inner aluminum plastic composite bag, outer kraft paper bag (or customer specified packaging)
Stored in dry and ventilated place
Prevent sun, rain and water
Storage period is 6 months